| 種類 | 規(guī)格/L262GC | ||
| 尼龍PA66 | |||
| 特性：玻纖增強(qiáng)，良好剛性，耐溫，良好流動(dòng)性和表面。 | |||
| 項(xiàng)目 | ASTM | 單位 | 打包 |
| Density | D-792 | 1.39 | |
| Melt index | D-1238 | g/10 min | 36.00 |
| D-790 | Mpa | 261 | |
| Flexural strength | |||
| D-790 | Mpa | 9251.97 | |
| Flexural modulus | |||
| D-256 | KJ/M2 | 11.07 | |
| Notched impact strength | |||
| D-638 | Mpa | 168.92 | |
| Tensile strength at break | |||
| D-638 | % | 3.44 | |
| Elongation at break | |||
| D-648 | ℃ | 240 | |
| Heat deflection temperature | |||
| UL-94 | HB | ||
| Flammability | |||
| 160℃/12min | % | 0.1 | |
| The moisture | |||
| ASH | % | 33.7 | |
| 模具收縮率 | % | 0.4-0.6 | |
| 參考成型工藝 | 干燥 | ℃ | 4小時(shí) |
| 成型溫度 | ℃ | ||
| 模具溫度 | ℃ | ||